Study the Mechanical Properties of (Al-Cu-Mg) Matrix Composites Reinforced by Alumina Particles
DOI:
https://doi.org/10.25130/tjps.v20i3.1199Keywords:
Heat Treatment Solution, official ageing , composite materialAbstract
The aim of the present research is studying the mechanical properties of composites matrix fabricated of aluminum (Al-4.5%Cu-1.5%Mg) by cast and to proceeding the heat treatment solution from different temperatures 500oC, 525oC and 550oC for different times 2hr and 4hr, and then proceeding the requil hardness (HBR), Therefore we conducted the optimum value from the alloy basic (A) at the temperature 550oC for 6hr time.
Also we prepared the matrix composite reinforced by alumina (Al2O3) with different percentage weight (1.5%-2.5%) and three different particles sizes (75µm≥63µm≥53µm≥0.1µm) which named as (A1, A2, B1, B2, C1, C2) according to their weight and size percentages, and then proceeding the heat treatment solution and official ageing about them at the temperature degree 550oC for 2hr and4hr.
Mechanical tests like hardness and Tensile resistance were conducted all of them reached that the composite material (A2) in which there weight and size percentages are 2.5% and ≥0.1µm have upper values of these test's, accordingly we concluded that the reduce particles means increased its rigidity, toughness and solidity.
Finally the microstructures tests shows that the prepared composites materials have small size as compared with microstructure of the basic cast alloys and the distribution of alumina particles was fairly homogeneous in the basic allot, also we showed that the heat treatment solutions and official ageing are affected at these composite materials and alloys.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Tikrit Journal of Pure Science
This work is licensed under a Creative Commons Attribution 4.0 International License.
Tikrit Journal of Pure Science is licensed under the Creative Commons Attribution 4.0 International License, which allows users to copy, create extracts, abstracts, and new works from the article, alter and revise the article, and make commercial use of the article (including reuse and/or resale of the article by commercial entities), provided the user gives appropriate credit (with a link to the formal publication through the relevant DOI), provides a link to the license, indicates if changes were made, and the licensor is not represented as endorsing the use made of the work. The authors hold the copyright for their published work on the Tikrit J. Pure Sci. website, while Tikrit J. Pure Sci. is responsible for appreciate citation of their work, which is released under CC-BY-4.0, enabling the unrestricted use, distribution, and reproduction of an article in any medium, provided that the original work is properly cited.