Growth, structural and magnetic properties of Gadolinium oxide (Gd2O3) thin films
DOI:
https://doi.org/10.25130/tjps.v25i5.296Abstract
Gd2O3 nanoparticles thin films obtain through the spin coating techniques deposited on substrate of p-Si(100) . The structural properties of the thin film were measured by X-ray diffraction technology (XRD) to know the crystal structure and the effect of the difference of different annealing temperatures on the crystal growth of these samples, and the scanning electron microscopy examinations (SEM) and the magnetic properties were studied using the Vibrating Sample Magnetometer(VSM) of Various annealing temperatures (500,600,700,800) ̊C. The results of the X-ray diffraction showed that all the prepared membranes have a multi-crystalline structure with different diffraction values and directions and the Gd2O3 thin film were of the cubic type and it was noted that by increasing the annealing temperature we get the best crystalline development and the results of SEM showed that the shape of the deposited nanoparticles was spherical, and we note an increase in the saturation magnetization (MS) about (0.1421 - 0.1811) emu / g with increased of annealing temperature.
Downloads
Published
How to Cite
License
Copyright (c) 2022 Tikrit Journal of Pure Science
This work is licensed under a Creative Commons Attribution 4.0 International License.
Tikrit Journal of Pure Science is licensed under the Creative Commons Attribution 4.0 International License, which allows users to copy, create extracts, abstracts, and new works from the article, alter and revise the article, and make commercial use of the article (including reuse and/or resale of the article by commercial entities), provided the user gives appropriate credit (with a link to the formal publication through the relevant DOI), provides a link to the license, indicates if changes were made, and the licensor is not represented as endorsing the use made of the work. The authors hold the copyright for their published work on the Tikrit J. Pure Sci. website, while Tikrit J. Pure Sci. is responsible for appreciate citation of their work, which is released under CC-BY-4.0, enabling the unrestricted use, distribution, and reproduction of an article in any medium, provided that the original work is properly cited.